Chlorine content:
|
35 ~ 37 % |
|---|---|
|
Heat of fusion:
|
≤ 2.0 J/g |
|
Residues on Sieve(0.8mm Sieve):
|
≤ 2.0 % |
|
Apparent density:
|
≥ 0.5 g/ml |
|
Bulk density:
|
≥ 0.5 g/ml |
|
Density/Specific weight:
|
1.17 ~ 1.21 g/cm3 |
|
Shore A Hardness:
|
≤ 60 |
|
Tensile strength:
|
≥ 8 Mpa |
|
Elongation at break:
|
≥ 700 % |
|
Mooney viscosity:
|
80 ~ 95 ML (1±4) 125 C |
|
Ash content:
|
≤ 4.5 % |
|
Stable time:
|
≥ 8 Min |
|
Impurity particles:
|
≤ 10 Unit/200g |
|
Packaging:
|
25 Kg/woven bag |
|
Volatile matter:
|
≤ 0.3 % |
|
Calcium Carbonate:
|
5 % |
CPE135A has excellent physical properties, including high toughness at low temperature, high tensile strength. It is rigid PVC impact modifier, with good anti-caking and rapid plasticity, properties and low temperature softening property and good mechanical property, widely used as PVC impact modifiers, ACR & MBS impact modifiers and also magnetic materials, films, sealing materials and waterproof rolls.
|
Chlorine content:
|
35 ~ 37 % |
|---|---|
|
Heat of fusion:
|
≤ 2.0 J/g |
|
Residues on Sieve(0.8mm Sieve):
|
≤ 2.0 % |
|
Apparent density:
|
≥ 0.5 g/ml |
|
Bulk density:
|
≥ 0.5 g/ml |
|
Density/Specific weight:
|
1.17 ~ 1.21 g/cm3 |
|
Shore A Hardness:
|
≤ 60 |
|
Tensile strength:
|
≥ 8 Mpa |
|
Elongation at break:
|
≥ 700 % |
|
Mooney viscosity:
|
80 ~ 95 ML (1±4) 125 C |
|
Ash content:
|
≤ 4.5 % |
|
Stable time:
|
≥ 8 Min |
|
Impurity particles:
|
≤ 10 Unit/200g |
|
Packaging:
|
25 Kg/woven bag |
|
Volatile matter:
|
≤ 0.3 % |
|
Calcium Carbonate:
|
5 % |
Chlorine content : 35 ~ 37%
Heat of fusion : ≤ 2.0 J/g
Residues on Sieve(0.8mm Sieve) : ≤ 2.0 %
Apparent density : ≥ 0.5 g/ml
Storage Life : 1-3 years
Min Order : 1 Ton
Average Lead Time : Peak Season Lead Time: one month Off Season Lead Time: within 15 workdays
Packaging : 25 kg
You can submit your orders using the following form.
You can contact us through the following form.
Reviews
There are no reviews yet.